Bijels
eBook - ePub

Bijels

Bicontinuous Particle-stabilized Emulsions

Paul S Clegg, Paul S Clegg

Condividi libro
  1. 246 pagine
  2. English
  3. ePUB (disponibile sull'app)
  4. Disponibile su iOS e Android
eBook - ePub

Bijels

Bicontinuous Particle-stabilized Emulsions

Paul S Clegg, Paul S Clegg

Dettagli del libro
Anteprima del libro
Indice dei contenuti
Citazioni

Informazioni sul libro

Bicontinuous interfacially jammed emulsion gels, now commonly termed 'bijels' are a class of soft materials, in which interpenetrating, continuous domains of two immiscible fluids are maintained in a rigid arrangement by a jammed layer of colloidal particles at their interface. Such gels have unusual material properties that promise exciting applications across diverse fields from energy materials and catalysis, to food science. This is the first book on the subject and provides the reader with a fundamental introduction to the field.

Edited by Paul Clegg, a recognised authority on bijels, the reader will learn about the bijeland its formation. Starting with three component systems, the reader will be introduced to systems using only two liquids and colloidal particles before moving onto more complex systems with additional components. These systems are looked at via both experimental and simulation studies, explaining phase separation kinetics, structure formation, properties and functionalisation. A closing section on bijel production using flow explores thin film and bulk structure formation relevant to larger scale materials design.

Bringing together current understanding this book aims to bring the potential application of bijels to diverse materials challenges closer to fruition. This is a must-have resource for anyone working in soft matter and applied fields.

Foreword by Michael E. Cates, Lucasian Professor of Mathematics at the University of Cambridge.

Domande frequenti

Come faccio ad annullare l'abbonamento?
È semplicissimo: basta accedere alla sezione Account nelle Impostazioni e cliccare su "Annulla abbonamento". Dopo la cancellazione, l'abbonamento rimarrà attivo per il periodo rimanente già pagato. Per maggiori informazioni, clicca qui
È possibile scaricare libri? Se sì, come?
Al momento è possibile scaricare tramite l'app tutti i nostri libri ePub mobile-friendly. Anche la maggior parte dei nostri PDF è scaricabile e stiamo lavorando per rendere disponibile quanto prima il download di tutti gli altri file. Per maggiori informazioni, clicca qui
Che differenza c'è tra i piani?
Entrambi i piani ti danno accesso illimitato alla libreria e a tutte le funzionalità di Perlego. Le uniche differenze sono il prezzo e il periodo di abbonamento: con il piano annuale risparmierai circa il 30% rispetto a 12 rate con quello mensile.
Cos'è Perlego?
Perlego è un servizio di abbonamento a testi accademici, che ti permette di accedere a un'intera libreria online a un prezzo inferiore rispetto a quello che pagheresti per acquistare un singolo libro al mese. Con oltre 1 milione di testi suddivisi in più di 1.000 categorie, troverai sicuramente ciò che fa per te! Per maggiori informazioni, clicca qui.
Perlego supporta la sintesi vocale?
Cerca l'icona Sintesi vocale nel prossimo libro che leggerai per verificare se è possibile riprodurre l'audio. Questo strumento permette di leggere il testo a voce alta, evidenziandolo man mano che la lettura procede. Puoi aumentare o diminuire la velocità della sintesi vocale, oppure sospendere la riproduzione. Per maggiori informazioni, clicca qui.
Bijels è disponibile online in formato PDF/ePub?
Sì, puoi accedere a Bijels di Paul S Clegg, Paul S Clegg in formato PDF e/o ePub, così come ad altri libri molto apprezzati nelle sezioni relative a Physical Sciences e Fluid Mechanics. Scopri oltre 1 milione di libri disponibili nel nostro catalogo.

Informazioni

Anno
2020
ISBN
9781839161223
Edizione
1
CHAPTER 1
Introduction to Bijels
P. S. Clegg* and J. H. J. Thijssen
SUPA School of Physics & Astronomy, The University of Edinburgh, Peter Guthrie Tait Road, Edinburgh, EH9 3FD, UK,
*E-mail: [email protected]

The bijel is a soft composite material with unusual characteristics that make it suitable, for example, for catalysis, filtration and electrode/electrolyte applications. The name is an acronym for bicontinuous interfacially jammed emulsion gel; it is a member of the family of emulsions with interfaces stabilized by colloidal particles. Conventional particle-stabilized (Pickering–Ramsden) emulsions have a dispersed liquid phase in the form of droplets and a continuous liquid phase that surrounds them. A bijel has two continuous liquid phases that are mutually entangled in a tortuous pattern, with a particle-stabilized interface between. Bijels were originally conceived in silico and conventionally fabricated by arresting the spinodal pattern of phase-separating liquids. The purpose of this chapter is to present the bijel concept as initially developed. This provides the foundation for the more recent innovations covered in subsequent chapters. We begin by putting the bijel idea in the context of the liquid-crystal research that immediately preceded it. We then explain the practicalities of making bijels, the processing route and the characteristics of the final samples. We briefly mention related research on freeze-casting porous ceramics, which occurred in parallel and is another example of using a phase transition in a host solvent to structure colloidal particles. Finally, we highlight some very recent research on carboxysomes, where self-organization driven by phase transition kinetics is being used in a very different context.

1.1 Background

Self-assembly of colloidal components is an important means of building materials and objects from the micrometre scale upwards. It is often achieved by controlling the chemical bonds formed between the components. 1 Most spectacularly, this has been implemented via the use of carefully chosen DNA segments that are attached to solid particle or droplet surfaces. 2 In this case, the DNA can be directly bonded to complementary strands or via the use of linker molecules. 3 The topic of this chapter is a profoundly different approach: organizing particles by using the phase transition kinetics of the host solvent. This has two advantages: firstly, the pattern of organization comes from the solvent and not from the building blocks. Hence, the same approach will work for a broad variety of starting materials. Secondly, because the approach relies on the host solvent being driven out of thermodynamic equilibrium, it is history-dependent. This makes it possible to tune the formation route via changes to parameters such as composition, quench depth, quench rate, etc. Organizing particles, by using the phase transition kinetics of the host solvent, makes it possible to achieve the same result using different particles and to controllably achieve different results using the same particles. This is a versatile approach. Towards the end of the chapter, we will see how organization via phase separation is being used to explain carboxysome formation in cyanobacteria. In this case, both specific interactions between components and generic phase separation are important.
The bijel forms when liquids that demix via spinodal decomposition are used to assemble particles. This research rose to prominence with the publication of computer simulations 4 in 2005 and their subsequent experimental realization in 2007. 5 However, the idea of structuring liquids using complex host solvents had been explored previously, for example, by working with composites of liquid crystals and colloidal particles. The soft matter group at the University of Edinburgh, led in turn by Pusey, Cates and then Poon, had spent many years studying dispersions of sterically stabilized poly(methyl methacrylate) colloidal particles (PMMA): firstly, as model hard spheres and, secondly, with non-adsorbing polymers as a model of colloidal depletion interactions. Meeker, Poon and collaborators went on to examine the behaviour of PMMA particles in a highly unconventional solvent. 6 Meeker et al. used a low-molecular-weight liquid crystal 4-n-pentyl-4′-cyanobiphenyl (5CB) that exhibits an isotropic to nematic phase transition at T IN ≈ 35 °C. The experiments using ∼5 vol% of particles revealed that a particle network formed during the temperature quench and that this conveyed great mechanical strength to the liquid crystal (Figure 1.1). Subsequent research explored the details of the network, its properties and its formation. 7
image
Figure 1.1 Network formation in a sample of 5CB with φ w = 0.05 of σ = 0.7 µm PMMA particles cooled through the isotropic–nematic transition at T IN down to T = 15 °C. After five minutes at this temperature, the samples were removed from the temperature stage. The resulting network structure was studied via fluorescence confocal microscopy using a Nikon microscope and the 488 nm line of an Ar-ion laser.
The research on 5CB–PMMA composites set the scene for the bijel project. The phase transition kinetics of the host solvent and the relationship between the particles and the ordered and disordered phases play crucial roles in structure self-organization. In the isotropic phase, molecular orientation is random, whereas, in the nematic phase, the molecules have a preference for alignment along a specific axis. On cooling, nuclei of ordered nematic appear and begin to confine the PMMA particles in the residual isotropic phase due to the elastic energy penalty of leaving a PMMA particle in a well-ordered nematic region. The nuclei progressively coarsen, which ultimately confines the particles in high volume fraction strands with disordered liquid crystal in the interstices.
At a conceptual level, the isotropic–nematic transition is characterized by a non-conserved order parameter. Once the phase transition has gone to completion, none of the high temperature disordered (isotropic) phase remains. Hence, particle network formation is what occurs as the particles are excluded from the ordered regions. The bijel project was then launched as the result of Cates (then also at the University of Edinburgh) asking the question: what would happen to particles dispersed in the disordered phase of a system characterized by a conserved order parameter? He then articulated some of the ideas subsequently researched and described in this book as claims in a patent filed in 2006. 8 At a transition with a conserved order parameter the aspects of the system that will go on to form the ordered phase already exist in the disordered phase. Phase-separating liquids are an example of just such a system. 4
Whether the order parameter is conserved or non-conserved has profound implications for the dynamics of the phase transition and this, in turn, is important when the transition is being employed to organize dispersed particles. When an order parameter is conserved through a phase transition, components have to move around within the sample for the order to develop. 9 In phase-separating liquids, this occurs via diffusion at an early stage and is then driven by Laplace pressure gradients during late-stage coarsening. 10 As a bijel begins to form, this is crucial because the incipient arrangement of particles must allow material to diffuse across the interface. Likewise, at a later stage during bijel formation the jammed particles must finally prevent large-scale flow parallel to the interface. By contrast, in a system characterized by a non-conserved order parameter, the phase transition dynamics do not involve components moving. However, this does not mean that nothing moves during the formation of, for example, liquid-crystal particle composites. As regions of the sample order, and as the order grows, the particulate component will be swept along by the ordering front. A crucial characteristic in this case is whether the particles have too much inertia to be moved by this ordering front. 11
As an aside, it is important to note that it is also possible to create cellular networks, such as those observed in 5CB–PMMA composites, in partially miscible binary fluid systems (see Figure 1.2), i.e., via a transition with a conserved order parameter. 12 In this case, emulsions are created via nucleation and growth following an off-critical quench of a dispersion of silica particles in an oil/alcohol mixture. Droplets of the minority phase form and particles are both swept up onto the liquid interface and trapped between the droplets. Here, the tuning of the particle wettability is not crucial and the emulsion has long-term stability from a combination of interfacial particles and a surplus population in the continuous phase. Network formation then occurs on re-warming the system towards the mixed phase. Due to creaming of the droplets, a change in (local) sample composition has occurred, with much of the continuous phase separated at the base of the sample. Hence, during warming the droplets expand, largely due to coalescence, and the particles become increasingly concentrated in the space between the droplets. A faceted network is found to form (see Figure 1.2).A similar change in sample composition, leading to network formation, can also be achieved via evaporation of one of the liquid phases from a particle-stabilized emulsion. 13
image
Figure 1.2 Three-dimensional structure from two-photon fluorescence images of the formation of a cellular network by step-wise heating of a creamed hexane–methanol/silica emulsion: (a,c,e) vertical xz slices and (b,d,f) horizontal xy slices; the latter were taken at the heights indicated by white arrows in panels a,c,e. Sample temperature was constant for ≥3 min prior to imaging; heating rates were ∼0.1 °C min−1. Scale bars: 200 µm. Reproduced from ref. 12 with permission from the Royal Society of Chemistry.
Returning to bijels, there are important experimental results that pre-date the fabrication of bijels from low-molecular-weight liquids. In 1994,Gubbels et al. used carbon black particles to stabilize a blend of polyethylene and polystyrene polymers. 14 They needed the carbon black particles to percolate through the sample to give good electrical conductivity. Unsurprisingly, the best blend stabilization and conductivity properties were achieved with the particles trapped at the interface between two tortuous polymer domains. In 2005, Composto and his team prepared two-dimensional bijels in thin polymer films (see Chapters 3 and 4). This geometry allowed them to explore the relationship between the morphology and the wettability of the external surfaces of the samples. While both of these projects resulted in the formation of polymer blend-based composites, the work on three-dimensional sam...